ISO 15608 Material Group 3.3
Precipitation-hardening fine-grained structural steels, but not stainless steels Precipitation hardening, or simply ‘hardening’, is a heat treatment comprising solution treatment and ageing. The hardening process is essentially based on the temperature-dependent solubility of the iron lattice for foreign atoms; in the case of unalloyed steels, these are mainly nitrogen atoms. These are responsible for thegenerally […]
Unlegierte und niedriglegierte Stähle der ISO 15608 Gruppe 1.1
Unlegierter kohlenstoffarmer Stahl mit einer bestimmten Mindeststreckgrenze mit ReH ≤ 275 N/mm2 a und mit der folgenden Analyse:C ≤ 0,25%; Si ≤ 0,60%; Mn ≤ 1,8%; Mo ≤ 0,70%b; S ≤ 0,045%; P ≤ 0,045%; Cu ≤ 0,40%b; Ni ≤ 0,5%b; Cr ≤ 0,3%b; (0,4% für Gusseisen; Nb ≤0,06%; V ≤ 0,1%b; Ti ≤0,05%; Anmerkungen: […]
Unlegierte C-Stähle mit 275 < ReH ≤ 360 N/mm2 – ISO 15608 Gruppe 1.2
Unlegierter kohlenstoffarmer Stahl mit einer Mindeststreckgrenze von 275 < ReH ≤ 360 N/mm2 a und mit der folgenden Analyse:C ≤ 0,25%; Si ≤ 0,60%; Mn ≤ 1,8%; Mo ≤ 0,70%b; S ≤ 0,045%; P ≤ 0,045%; Cu ≤ 0,40%b; Ni ≤ 0,5%b; Cr ≤ 0,3%b; (0,4% für Gusseisen; Nb ≤0,06%; V ≤ 0,1%b; Ti ≤0,05%; […]
Normalisierte Feinkornbaustähle ISO 15608 Werkstoffgruppe 1.3
Normalisierter Feinkornbaustähle mit einer Mindeststreckgrenze von ReH > 360 N/mm2 a und mit der folgenden Analyse:C ≤ 0,25%; Si ≤ 0,60%; Mn ≤ 1,8%; Mo ≤ 0,70%b; S ≤ 0,045%; P ≤ 0,045%; Cu ≤ 0,40%b; Ni ≤ 0,5%b; Cr ≤ 0,3%b; (0,4% für Gusseisen; Nb ≤0,06%; V ≤ 0,1%b; Ti ≤0,05%; Anmerkungen: a Gemäß […]
Wetterfeste Stähle ISO 15608 Werkstoffgruppe 1.4
Wetterfeste Stähle sind in der Materialgruppe 1.4 der Norm ISO 15608 aufgeführt und zeichnen sich durch eine verbesserte Korrosionsbeständigkeit in der Atmosphäre aus, wobei die Analysewerte die Anforderungen für die einzelnen Elemente, wie sie in den anderen Werkstoffgruppen 1.1, 1.2 und 1.3, angegeben sind, übersteigen können. Was sind wetterfeste Stähle, wie sie in der Werkstoffgruppe […]
ISO 15608 Material Group 2.1
ISO 15608 Material Group 2.1 : Thermomechanically treated fine-grain steels and cast steels with a specific minimum yield strength 360 < ReH ≤ 460 N/mm2. Thermomechanically steels (TM) rolled fine-grain structural steels is characterised by a high minimum yield strength ReH by good weldability. What is the thermomechnical (TM) process? Exceptionally low alloying-element contents, expressed […]
EN ISO 15608 Material Group 2.2
EN ISO 15608 Material Group 2.2: Thermomechanically treated fine-grain steels (TM steel) and cast steels with a specific minimum yield strength ReH > 460 N/mm2. Thermomechanically steels (TM) rolled fine-grain structural steels are characterised at a high yield strength by good weldability. Thermomechanically steels (TM) rolled fine-grain structural steels is characterised by a high minimum […]
ISO 15608 Material Group 3.1
High strength low alloy steel ISO 15608 Material Group 3.1: Quenched and tempered (QT) fine-grain high strength low alloy steel with a specific minimum yield strength 360 < ReH ≤ 690 N/mm2. What is the quenched and tempering (QT) process of high strength low alloy steel? Quenching and tempering is a heat-treatment method for high […]
ISO 15608 Material Group 3.2
ISO 15608 Material Group 3.2: Quenched and tempered (QT) fine-grain high strength steels with a specific minimum yield strength ReH > 690 N/mm2. What is the quenched and tempering (QT) process of high strength steels? Quenching and tempering is a heat-treatment method for high strength low alloy steel. Quenching and tempering consists of a two-stage heat-treatment process. Stage […]
ISO 15608 Material Group 4.1
ISO 15608 Material Group 4.1: HSLA steel – Low vanadium alloyed Cr-Mo-(Ni) steels with Mo ≤ 0,7 %, V ≤ 0,1 %, Cr ≤ 0,3 % and Ni ≤ 0,7 % Features of high strength low-allow steels (HSLA steel) material group 4.1 This group contain high strength low-alloy steels (HSLA) with specified yield strength (see […]